HX-8810 two-component structural silicone sealant meets or exceeds the requirements of the following specification:
ASTM specifications:
C1184, type S
C920, tyoe S
European Standard:
ETAG 002
China Standard:
GB 16776
Adhesion
HX-8810 exhibits excellent primerless adhesion to many substrates, e.g. glass, tiles, ceramics, enamel, glazed tiles and clinker; metal, e.g. aluminium, steel, zinc or copper; impregnated, varnished or painted wood; and many plastics.
Users must carry out their own tests due to the great variety of substances.
The adhesion can be improved in many cases by pretreatment of the substrates with a primer.
Restrictions on use
HX-8810 may be discolored in contact with some organic elastomers, e.g. EPDM, APTK and neoprene.
HX-8810 is not recommended for use on natural stone, such as marble, granite, quartzite, as it can cause staining.
HX-8810 is not recommended for sealing of joints continuous immersed in water.
HX-8810 can not in contact with food.
The curing time can be adjusted by change the rate of Part II and not influenced by humidity.
Product data
Property | Unit | Value |
Part I | ||
Color | White | |
Density at 23C | [g/cm3] | 1.33 |
Part II | ||
Color | Black | |
Mixed by rate:10:1~12:1 | ||
Color | Black | |
Density at 23C | [g/cm3] | 1.33 |
Tooling time (23C/50% r.h.) | min | 10~30 |
Skin-forming time at 23C/50% r.h. | min | 25~45 |
Tack free time at 23C/50% r.h. | min | 50~90 |
Consistency | Non-sag | |
Hardness, Shore A | SHA | 45 |
Tensile strength | [N/mm2] | 1.10 |
Ultimate elongation | [%] | 250 |
Joint movement capability | [%] | ±25 |
(These figures are intended as a guide and should not be used in preparing specifications)